1. The longitudinal tear in the middle of the steel belt is 14-15 meters, how to repair it?
The upper and lower covering glue of the damaged part can be peeled off (the length exceeds the damaged part by 50-100mm, and the width exceeds the damaged part by 30-50mm), and at the same time, take a piece of rubber with the same size as the peeled part (preferably with a layer of cloth), and then It can be repaired according to the cold glue method.
2. Comparison of EP high temperature resistant belt and cotton canvas high temperature resistant belt:
a. The same point: the surface covering glue is the same.
b. Differences: cotton canvas can withstand a maximum temperature of 150 degree ; EP-TNG canvas can be used for a long time at 200 degree , and can be used at a maximum of 220 degree ;
The strength of cotton canvas is relatively low, only 50N/mm; while the strength of EP-TNG canvas is relatively high, and the commonly used type 200 is 200N/mm;
Адгезия термостойкой ленты из хлопкового полотна относительно низкая, а адгезия термостойкой ленты EP относительно высокая; срок службы термостойкой ленты EP, очевидно, больше, чем у ленты из хлопчатобумажной ткани, стойкой к высоким температурам.
3. Hot glue stripping method (is it good to remove the glue at one end)?
Это еще один способ склейки, такой способ тоже возможен, но если вы используете этот способ, обратите внимание на следующие моменты:
a. Be sure to use sealing glue;
b. The parts where the edge rubber parts meet must be connected by vulcanized rubber;
c. The parts where the rubber is connected must be polished
The disadvantage is that the edge glue part is easily damaged if it is not handled properly.
4. The joint temperature reaches 120 degree , but does not reach the normal vulcanization temperature?
no. The normal vulcanization and crosslinking temperature of rubber is determined by the vulcanizing agent and accelerator in the rubber. In order to ensure the safety of rubber processing, the general manufacturer will not set the vulcanization starting temperature of the rubber used in the conveyor belt to be very low. Therefore, when the temperature reaches 120 degree , the rubber will not enter the normal vulcanization state. Therefore, at 120 degree , the quality of the conveyor belt joint will be greatly affected.
Обычно, когда температура вулканизации выше, чем критическая температура вулканизации ускорителя и вулканизирующего агента, и не может достичь нормальной температуры вулканизации, можно применить метод продления времени вулканизации, чтобы вулканизация каучука соответствовала требованиям. Как правило, каждый раз, когда температура ниже 10 градусов, время вулканизации увеличивается в 2-4 раза. Конечно, из соображений производительности мы не рекомендуем использовать низкую-температуру и длительную вулканизацию.
5. Can core rubbers from different manufacturers be mixed?
Не рекомендуется смешивать резину сердечника разных производителей, потому что рецептура резины сердечника разных производителей отличается. В каучуке есть много видов компаундирующих агентов, и некоторые из них имеют интерактивные реакции. В формулах одного и того же производителя не будет компаундирующих агентов с побочными интерактивными реакциями, но формулы разных производителей сильно отличаются. При использовании могут возникнуть интерактивные отражения компаундирующих агентов, которые повлияют на эффект использования резинового сердечника.